Title:Effect of nanostructure on thermoelectric properties of La$_{0.7}$Sr$_{0.3}$MnO$_{3}$ in 300-600 K range
View PDFAbstract:In oxide materials, nanostructuring effect has been found very promising approach for the enhancement of \textit{figure-of-merit}, \textit{ZT}. In the present work, we have synthesized La$_{0.7}$Sr$_{0.3}$MnO$_{3}$ (LSMO) compound using sol-gel method and samples of crystallite size of 34, 41, and 49 nm were obtained by giving different heat treatment. Seebeck coefficient ($\alpha$), electrical resistivity ($\rho$), and thermal conductivity ($\kappa$) measurements were carried out in 300-600 K temperature range. The systematic change in the values of $\alpha$ from $\sim$ -19 $\mu$V/K to $\sim$ -24 $\mu$V/K and drastic reduction in the values of $\kappa$ from $\sim$0.88 W/mK to $\sim$0.23 W/mK are observed as crystallite size is reduced from 49 nm to 34 nm at $\sim$600 K. Also, fall in the values of $\rho$ in the paramagnetic (PM) insulator phase (400-600 K) are effectively responsible for the increasing trend in the values of \textit{ZT} at high temperature. For the crystallite size of 41 nm, value of \textit{ZT} at 600 K was found to be $\sim$0.017, which can be further increased up to $\sim$0.045 around 650 K temperature. The predicted value of \textit{ZT} suggests that LSMO can be suitable oxide material for thermoelectric applications at high temperature.
Submission history
From: Saurabh Singh [view email][v1] Thu, 21 Sep 2017 08:24:10 UTC (106 KB)
[v2] Wed, 4 Oct 2017 11:52:34 UTC (106 KB)
Current browse context:
physics.app-ph
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.