[Submitted on 30 Apr 2009]
Title:Structural, optical, magnetic and electrical properties of Zn1-x Co (x) O thin films
View PDFAbstract: Despite a considerable effort aiming at elucidating the nature of ferromagnetism in ZnO-based magnetic semiconductor, its origin still remains debatable. Although the observation of above room temperature ferromagnetism has been reported frequently in the literature by magnetometry measurement, so far there has been no report on correlated ferromagnetism in magnetic, optical and electrical measurements. In this paper, we investigate systematically the structural, optical, magnetic and electrical properties of Zn1-x Co (x) O:Al thin films prepared by sputtering with x ranging from 0 to 0.33. We show that correlated ferromagnetism is present only in samples with x > 0.25. In contrast, samples with x < 0.2 exhibit weak ferromagnetism only in magnetometry measurement which is absent in optical and electrical measurements. We demonstrate, by systematic electrical transport studies that carrier localization indeed occurs below 20-50 K for samples with x < 0.2; however, this does not lead to the formation of ferromagnetic phase in these samples with an electron concentration in the range of 6 x 10(19) cm(-3) 1 x 10(20) cm(-3). Detailed structural and optical transmission spectroscopy analyses revealed that the anomalous Hall effect observed in samples with x > 0.25 is due to the formation of secondary phases and Co clusters.
Current browse context:
cond-mat.mtrl-sci
Change to browse by:
References & Citations
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
IArxiv Recommender
(What is IArxiv?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.