SQUIDs based set-up for probing current noise and correlations in three-terminal devices
Authors:
A. H. Pfeffer,
B. Kaviraj,
O. Coupiac,
F. Lefloch
Abstract:
We have implemented a new experimental set-up for precise measurements of current fluctuations in three-terminal devices. The system operates at very low temperatures (30 mK) and is equipped with three SQUIDs as low noise current amplifiers. A SQUID input coil is connected to each terminal of a sample allowing the acquisition of time-dependent current everywhere in the circuit. From these traces,…
▽ More
We have implemented a new experimental set-up for precise measurements of current fluctuations in three-terminal devices. The system operates at very low temperatures (30 mK) and is equipped with three SQUIDs as low noise current amplifiers. A SQUID input coil is connected to each terminal of a sample allowing the acquisition of time-dependent current everywhere in the circuit. From these traces, we can measure the current mean value, the noise and cross-correlations between different branches of a device. In this paper we present calibration results of noise and cross-correlations obtained using low impedance macroscopic resistors. From these results we can extract the noise level of the set-up and show that there are no intrinsic correlations due to the measurement scheme. We also studied noise and correlations as a function of a DC current and estimated the electronic temperature of various macroscopic resistors.
△ Less
Submitted 25 October, 2012;
originally announced October 2012.
-
Noise Correlations in Three-Terminal Diffusive Superconductor-Normal Metal-Superconductor Nanostructures
Authors:
B. Kaviraj,
O. Coupiac,
H. Courtois,
F. Lefloch
Abstract:
We present measurements of current noise and cross-correlations in three-terminal Superconductor-Normal metal-Superconductor (S-N-S) nanostructures that are potential solid-state entanglers thanks to Andreev reflections at the N-S interfaces. The noise correlation measurements spanned from the regime where electron-electron interactions are relevant to the regime of Incoherent Multiple Andreev Ref…
▽ More
We present measurements of current noise and cross-correlations in three-terminal Superconductor-Normal metal-Superconductor (S-N-S) nanostructures that are potential solid-state entanglers thanks to Andreev reflections at the N-S interfaces. The noise correlation measurements spanned from the regime where electron-electron interactions are relevant to the regime of Incoherent Multiple Andreev Reflection (IMAR). In the latter regime, negative cross-correlations are observed in samples with closely-spaced junctions.
△ Less
Submitted 18 August, 2011; v1 submitted 21 April, 2011;
originally announced April 2011.
-
Performances of a Newly High Sensitive Trilayer F/Cu/F GMI Sensor
Authors:
F. Alves,
B. Kaviraj,
L. Abi Rached,
J. Moutoussamy,
C. Coillot
Abstract:
We have selected stress-annealed nanocrystalline Fe-based ribbons for ferromagnetic/copper/ferromagnetic sensors exhibiting high magneto-impedance ratio. Longitudinal magneto-impedance reaches 400% at 60 kHz and longitudinal magneto-resistance increases up to 1300% around 200 kHz.
We have selected stress-annealed nanocrystalline Fe-based ribbons for ferromagnetic/copper/ferromagnetic sensors exhibiting high magneto-impedance ratio. Longitudinal magneto-impedance reaches 400% at 60 kHz and longitudinal magneto-resistance increases up to 1300% around 200 kHz.
△ Less
Submitted 8 October, 2007; v1 submitted 28 July, 2007;
originally announced July 2007.
-
Giant Magneto-impedance in stress-annealed Finemet/Copper/Finemet based trilayer structures
Authors:
B. Kaviraj,
F. Alves
Abstract:
The resistive and reactive components of magneto-impedance (MI) for Finemet/Copper/Finemet sandwiched structures based on stress-annealed nanocrystalline Fe75Si15B6Cu1Nb3 ribbons as functions of different fields (longitudinal and perpendicular) and frequencies have been measured and analyzed. Maximum magneto-resistance and magneto-inductance ratios of 700% and 450% have been obtained in 30-600 k…
▽ More
The resistive and reactive components of magneto-impedance (MI) for Finemet/Copper/Finemet sandwiched structures based on stress-annealed nanocrystalline Fe75Si15B6Cu1Nb3 ribbons as functions of different fields (longitudinal and perpendicular) and frequencies have been measured and analyzed. Maximum magneto-resistance and magneto-inductance ratios of 700% and 450% have been obtained in 30-600 kHz frequency range respectively. These large magneto-resistance and magneto-inductive ratios are a direct consequence of the large effective relative permeability due to the closed magnetic flux path in the trilayer structure. The influence of perpendicular bias fields (Hper) in the Longitudinal Magneto-impedance (LMI) configuration greatly improves the MI ratios and sensitivities. The maximum MI ratio for the resistive part increases to as large as 2500% for Hper ~ 1 Oe. The sensitivity of the magneto-resistance increases from 48%/Oe to 288%/Oe at 600 kHz frequency with the application of Hper ~ 30 Oe. Such high increase in MI ratios and sensitivities with perpendicular bias fields are due to the formation the favourable (transverse) domain structures.
△ Less
Submitted 28 July, 2007;
originally announced July 2007.
-
Simulation of stress-impedance effects in low magnetostrictive films
Authors:
B. Kaviraj,
S. K. Ghatak
Abstract:
A theoretical study of stress-impedance effect based on the solution of Landau-Lifsitz-Gilbert equation has been carried out. The results show that stress impedance effects depend largely on several extrinsic (external bias field, external frequency) and intrinsic (orientation and magnitude of uniaxial anisotropy, damping) parameters.
A theoretical study of stress-impedance effect based on the solution of Landau-Lifsitz-Gilbert equation has been carried out. The results show that stress impedance effects depend largely on several extrinsic (external bias field, external frequency) and intrinsic (orientation and magnitude of uniaxial anisotropy, damping) parameters.
△ Less
Submitted 22 August, 2006;
originally announced August 2006.
-
Influence of stress on magneto-impedance in Co71-xFexCr7Si8B14 (x = 0, 2) amorphous ribbons
Authors:
B. Kaviraj,
S. K. Ghatak
Abstract:
Systematic measurements of stress-impedance (SI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The impedance, Z for both the samples was found to be very sensitive functions of applied tensile stresses (up to 100MPa) exhibiting a maximum SI ratio as much as 80%…
▽ More
Systematic measurements of stress-impedance (SI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The impedance, Z for both the samples was found to be very sensitive functions of applied tensile stresses (up to 100MPa) exhibiting a maximum SI ratio as much as 80% at low frequency ~ 0.1MHz. The nature of variation of SI changes with the excitation frequency especially at higher frequencies in MHz region where it exhibits a peak. Magnetization measurements were also performed to observe the effects of applied stresses and magnetization decreased with the application of stress confirming the negative magnetostriction co-efficient of both the samples. Both the samples exhibited negative magneto-impedance (MI) when the variation of Z is observed with the applied bias magnetic field, H. The impedance as functions of applied magnetic field, Z(H), decreases with the application of stress thus making the MI curves broader. Maximum MI ratio as large as 99% has been observed for both the samples at low fields ~ 27Oe.
△ Less
Submitted 22 August, 2006;
originally announced August 2006.
-
Very large Magneto-impedance and its scaling behavior in amorphous Fe73.5Nb3Cu1Si13.5B9 ribbon
Authors:
B. Kaviraj,
S. K. Ghatak
Abstract:
Magneto-impedance (MI) effects have been observed for amorphous Fe73.5Nb3Cu1Si13.5B9 ribbon which has been excited by an a.c. magnetic field parallel to the length of the ribbon. Maximum relative change in MI as large as -99% was observed which has never been reported before. The relative change in MI, when plotted against scaled field was found to be nearly frequency independent. A phenomenolog…
▽ More
Magneto-impedance (MI) effects have been observed for amorphous Fe73.5Nb3Cu1Si13.5B9 ribbon which has been excited by an a.c. magnetic field parallel to the length of the ribbon. Maximum relative change in MI as large as -99% was observed which has never been reported before. The relative change in MI, when plotted against scaled field was found to be nearly frequency independent. A phenomenological formula for magneto-impedance, Z(H), in a ferromagnetic material, is proposed based on Pade approximant to describe the scaled behavior of MI.
△ Less
Submitted 8 October, 2007; v1 submitted 8 June, 2006;
originally announced June 2006.
-
Excitation Amplitude Dependence of Low Frequency Magneto-impedance of Amorphous Fe73.5Nb3Cu1Si13.5B9 Ribbon
Authors:
B. Kaviraj,
S. K. Ghatak
Abstract:
Magneto-impedance (MI) of soft ferromagnetic materials is a sensitive function of the amplitude and frequency of exciting a.c magnetic field. MI (Z) of amorphous ferromagnetic ribbon of nominal composition Fe73.5Nb3 Cu1 Si13.5 B9 is measured at different excitation currents with frequency ranging from 30kHz to 120KHz The excitation (a.c) and biasing (d.c) magnetic fields Hdc are parallel to ribb…
▽ More
Magneto-impedance (MI) of soft ferromagnetic materials is a sensitive function of the amplitude and frequency of exciting a.c magnetic field. MI (Z) of amorphous ferromagnetic ribbon of nominal composition Fe73.5Nb3 Cu1 Si13.5 B9 is measured at different excitation currents with frequency ranging from 30kHz to 120KHz The excitation (a.c) and biasing (d.c) magnetic fields Hdc are parallel to ribbon axis. At zero dc fields, Z exhibits non-linear dependence on excitation amplitude whereas at higher d.c fields (9Oe) Z is nearly independent of excitation amplitude. The impedance is maximum at zero bias field and sharply decreases as Hdc increases and almost zero hysterisis has been observed as Hdc is scanned. The maximum relative change of impedance (Z(H)-Z(H=0))/Z(H=0) is found to increase from nearly 45 to 60 percent when the excitation fields goes up from 14A/m to 140A/m. The large MI is associated with screening of electromagnetic field by magnetization induced by exciting ac field.
△ Less
Submitted 19 April, 2006;
originally announced April 2006.
-
Stress - and Magneto-Impedance in Co71-xFexCr7Si8B14 (x = 0, 2) amorphous ribbons
Authors:
B. Kaviraj,
S. K. Ghatak
Abstract:
Systematic measurements of stress impedance (SI) and magneto-impedance (MI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The impedance, Z, for both the samples was found to be very sensitive functions of applied tensile stress (up to 100MPa) exhibiting a maximu…
▽ More
Systematic measurements of stress impedance (SI) and magneto-impedance (MI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The impedance, Z, for both the samples was found to be very sensitive functions of applied tensile stress (up to 100MPa) exhibiting a maximum SI ratio as much as 80% at low frequency ~ 0.1MHz. The nature of variation of impedance, Z, changes with the excitation frequency especially at higher frequencies in MHz region where it exhibits a peak. Magnetization measurements were also performed to observe the effects of applied stress and magnetization decreases with the application of stress confirming the negative magnetostriction co-efficient of both the samples. Both the samples exhibited negative magneto-impedance when the variation of Z is observed with the applied bias magnetic field, H. Maximum MI ratio as large as 99% has been observed for both the samples at low fields ~ 27Oe. The impedance as functions of applied magnetic field, Z(H), decreases with the application of stress thus making the MI curves broader. Based on the electromagnetic screening and magnetization dynamics and incorporating the Gilbert and the Bloch-Bloembergen damping and stress dependent anisotropy, the SI has been calculated and is found to describe well the stress and field dependence of impedance of the two samples.
△ Less
Submitted 22 August, 2006; v1 submitted 19 April, 2006;
originally announced April 2006.
-
Influence of microwave annealing on GMI response and magnetization of an amorphous Fe73.5Nb3Cu1Si13.5B9 ribbon
Authors:
B. Kaviraj,
S. K Ghatak
Abstract:
The resistive and reactive components of magneto-impedance was studied for the as-quenched and microwave annealed amorphous Fe73.5Nb3Cu1Si13.5B9 ribbon as a function of biasing d.c magnetic fields (-60 to +60 Oe) and excitation frequencies (0.1, 1, 10 and 20MHz). The magneto-impedance (both components) response was much reduced for the microwave annealed ribbon and the changes were more discerna…
▽ More
The resistive and reactive components of magneto-impedance was studied for the as-quenched and microwave annealed amorphous Fe73.5Nb3Cu1Si13.5B9 ribbon as a function of biasing d.c magnetic fields (-60 to +60 Oe) and excitation frequencies (0.1, 1, 10 and 20MHz). The magneto-impedance (both components) response was much reduced for the microwave annealed ribbon and the changes were more discernable at higher excitation frequencies. The imaginary component of magneto-impedance showed maxima at finite (non-zero) d.c magnetic fields for both the as-quenched and microwave annealed ribbons. Magnetization measurements performed for both the as-quenched and microwave annealed ribbons revealed the magnetic hardness of the latter. The initial susceptibility decreases by two orders of magnitude for the microwave-annealed ribbon. XRD measurements indicated the transformation of the surface of the ribbon from the amorphous state to the crystalline one.
△ Less
Submitted 5 January, 2007; v1 submitted 15 April, 2006;
originally announced April 2006.
-
Anisotropic Dependence of Giant Magneto-Impedance of Amorphous Ferromagnetic Ribbon on Biasing Field
Authors:
B. Kaviraj,
S. K. Ghatak
Abstract:
The magneto-impedance (MI) in amorphous ribbon of nominal composition Fe73.5Nb3Cu1Si13.5B9 has been measured at 1MHz and at room temperature for different configurations of exciting a.c and biasing d.c. fields. A large drop in both resistance and reactance is observed as a function of d.c magnetic field. When the d.c and a.c fields are parallel but normal to the axis of ribbon, smaller magnetic…
▽ More
The magneto-impedance (MI) in amorphous ribbon of nominal composition Fe73.5Nb3Cu1Si13.5B9 has been measured at 1MHz and at room temperature for different configurations of exciting a.c and biasing d.c. fields. A large drop in both resistance and reactance is observed as a function of d.c magnetic field. When the d.c and a.c fields are parallel but normal to the axis of ribbon, smaller magnetic field is needed to reduce the impedance to its small saturated value compared to the situation when fields are along the axis of ribbon. Larger d.c. field is required to lower the impedance when the d.c field acts perpendicular to the plane of the ribbon. Such anisotropy in magneto-impedance is related to the anisotropic response of the magnetization of ribbon. The large change of impedance is attributed to large variation of a.c permeability on the direction and magnitude of the dc biasing field.
△ Less
Submitted 5 January, 2007; v1 submitted 15 April, 2006;
originally announced April 2006.
-
Magnetic Field and Displacement sensor based on Giant Magneto-impedance effect
Authors:
B. Kaviraj,
S. K. Ghatak
Abstract:
A two-core transducer assembly using a Fe73.5Nb3Cu1Si13.5B9 ribbon to detect a change of magnetic field is proposed and tested for displacement (linear and angular) and current sensor. Two identical inductors, with the ribbon as core, are a part of two series resonance network, and are in high impedance state when excited by a small a.c field of 1MHz in absence of d.c biasing field (Hdc). When t…
▽ More
A two-core transducer assembly using a Fe73.5Nb3Cu1Si13.5B9 ribbon to detect a change of magnetic field is proposed and tested for displacement (linear and angular) and current sensor. Two identical inductors, with the ribbon as core, are a part of two series resonance network, and are in high impedance state when excited by a small a.c field of 1MHz in absence of d.c biasing field (Hdc). When the magnetic state of one inductor is altered by biasing field, produced by a bar magnet or current carrying coil, an ac signal proportional to Hdc is generated by transducer. The results for the sensitivity and linearity with displacement (linear and angular) of a magnet and with field from the current carrying coil are presented for two particular configurations of the transducer. High sensitivities of voltage response as much as 12micro-volt/micro-meter and 3mV/degree have been obtained for the transducer as a linear and angular displacement sensor respectively in the transverse configuration of exciting a.c and biasing d.c fields.
△ Less
Submitted 8 January, 2007; v1 submitted 15 April, 2006;
originally announced April 2006.
-
Giant magneto-impedance in Ag-doped La0.7Sr0.3MnO3
Authors:
S. K. Ghatak,
B. Kaviraj,
T. K. Dey
Abstract:
The resistive and reactive parts of the magneto-impedance of sintered ferromagnetic samples of La0.7Sr0.3-xAgxMnO3 (x = 0.05, 0.25) have been measured at room temperature (<Tc) over frequency interval 1KHz to 15MHz and in presence of magnetic field up to 4KOe. The field dependence of relative change in resistance is small in KHz region but increases strongly for higher frequency of excitation. T…
▽ More
The resistive and reactive parts of the magneto-impedance of sintered ferromagnetic samples of La0.7Sr0.3-xAgxMnO3 (x = 0.05, 0.25) have been measured at room temperature (<Tc) over frequency interval 1KHz to 15MHz and in presence of magnetic field up to 4KOe. The field dependence of relative change in resistance is small in KHz region but increases strongly for higher frequency of excitation. The maximum value of relative change in resistance at H =4KOe was found to be around 70% at 15MHz frequency.On the contrary the corresponding change in reactance has less frequency sensitivity and the maximum occurs at 1MHz frequency. The magneto-impedance is negative for all frequencies. The 'normalized magneto-impedance' as defined by [Z(H)-Z(0)]/[Z(0)-Z(4K)] when plotted against scaled field H/H1/2 is found to be frequency independent ; H1/2 is the field where 'normalized magneto-impedance' is reduced to half its maximum. A phenomenological formula for magneto-impedance Z (H) in ferromagnetic material is proposed based on Pade approximant. The formula for Z (H) predicts the scaled behavior of 'normalized magneto-impedance'.
△ Less
Submitted 31 December, 2006; v1 submitted 6 April, 2006;
originally announced April 2006.